Home» Products» Flame Retardant Polyethylene(Poly Ethylene) » Flame Retardant PE Granules(1.6 mm V0)
Product List

Flame Retardant PE Granules(1.6 mm V0)

Description
Adopting PE as the base resin and evenly mixing it with antioxidant, flame retardant and processing modifier in a high speed, flame retardant flame retardant PE granules come into being after twin-screw kneading granulation. Its flame retardant grade reaches UL94 V-0 (1.6 mm). Flame retardant polyethylene granules possess the advantages of excellent resistance to stress cracking, low temperature resistance and impact resistance. They are widely applied in home appliances, auto spare parts, wire and cable, thermoplastic casing, home appliances shell and car inner decoration, etc. With advanced technological equipment, tremendous technical strength and reliable product quality, our flame retardant PE granules or flame retardant polyethylene granules have received a number of favorable comments from customers.

Technical Specifications


Properties
ASTM Test Condition Unit Typical Values
Physical Properties
Density D-792 23℃ g/cm3 1.20
Melt Flow Index D-1238 230℃ / 2.16 kg g/10min 0.1-3
Mold Shrinkage D-955 23℃ % 1.0-1.5
Mechanical Properties of Flame Retardant PE Granules
Tensile Strength D-638 10 mm / min MPa 18
Elongation at Break D-638 10 mm / min % 150
Flexural Strength D-790 2 mm / min MPa 20
Flexural Modulus D-790 2 mm / min MPa 400
IZOD Impact Strength Notched D-256 3.2 mm, 23℃ KJ/m2 10
Thermal Properties
Heat Distortion Temperature D-648 0.45 MPa, 6.4 mm 50
Others
Flammability UL-94 1.6 mm V0

Note: Typical values are the average data from laboratory. They are only for use reference and are not the standards for products.

Processing Conditions ofFlame Retardant PE Granules(1.6 mm V0)

Unit Range
Melt Temperature 110-150
Barrel Temperature Rear 110-140
Center 120-140
Front 130-150
Mold Temperature. 40
Mold Pressure   Pre-dry Requirements 60-80℃, 2-4 h

Note: The above-mentioned data is just for injection molding machine. According to different models, molds and specific requirementss of  flame retardant PE granules, we can make appropriate adjustments.

 

Shanghai Info New Material Technology Co., Ltd. is a high-tech enterprise engaged in research and development, sale and technical service of flame retardant polyethylene granules in China. We are also specialized in producing various high performance and functional modified plastic particles, sheets and film products, such as PP+POE granules, PP granules, PP+EPDM granules, polyethylene hydroxide granules, PE + magnesium hydrate granules, PE + aluminum hydrate granules, etc. Our company has a professional technical team of first-class rich experience and well-trained technicians. Our flame retardant PE granules or polyethylene granules have been exported to mainland, Hong Kong, Macao and Taiwan regions, North America, South America, Western Europe, Eastern Europe, East Asia, Southeast Asia, Middle East, Africa, Oceania, etc.

  • Halogen Free Flame Retardant PP+POE Granules(V0)
  • Halogen Free Flame Retardant PP+POE Granules (V0)As the base resin, PP is evenly mixed with fire retardant, POE (Polyolefin Elastomer) and processing modifier in a high speed. After twin-screw kneading granulation, halogen free flame retardant PP+POE granules (halogen free flame retardant compound) come into being. Its flammability level is UL94 V-0 (1.6 mm). This flame retardant plastic granule is well known for its excellent mechanical strength, excellent resistance to stress cracking, heat resistance and good workability. It is widely used in home ....